Zirconium oxide is used due to its polymorphism. It exists in three phases: monoclinic, tetragonal and cubic. Cooling to the monoclinic phase after sintering causes a large volume change, which often causes stress fractures in pure zirconia. Additives such as magnesia, calcia and yttria are used in the manufacture of the knife material to stabilize the high-temperature phases and minimize this volume change. The highest strength and toughness is produced by the addition of 3 mol% yttrium oxide yielding partially stabilized zirconia. This material consists of a mixture of tetragonal and cubic phases with a bending strength of nearly 1,200 MPa. Small cracks allow phase transformations to occur, which essentially close the cracks and prevent catastrophic failure, resulting in a relatively tough ceramic material, sometimes known as TTZ (transformation-toughened zirconia).
Ceramic knives are substantially harder than steel knives, will not corrode in harsh environments, are non-magnetic, and do not conduct electricity at room temperature. Because of their resistance to strong acid and caustic substances, and their ability to retain a cutting edge longer than forged metal knives, ceramic knives are better suited for slicing boneless meat, vegetables, fruit and bread. Since ceramics are brittle, blades may break if dropped on a hard surface although better manufacturing processes have reduced this risk. They are also unsuitable for chopping through bones, or frozen foods, or in other applications which require prying, which may result in chipping. Several brands now offer either a black-coloured or a designed blade made through an additional hot isostatic pressing step, which increases the toughness.
Sharpening and general care
Unlike a traditional steel blade that benefits from regular honing and resharpening in order to keep a sharp edge, a ceramic knife will stay sharp and retain its cutting edge for much longer—up to 10x longer according to some tests. The inherent hardness of the ceramic material also makes it more difficult for the consumer to resharpen. Although a ceramic knife therefore does not need regular sharpening in the same way as steel, its blade edge will eventually degrade or chip and lose its cutting edge, at which point specialized sharpening services are required for the ceramic edge.
Next: No Information
- CNC Tool Grinding Of "self-reliance"
- Endless New Cutting Tool Material
- Wear Resistance And Toughness Of Ce...
- Performance Optimization Of Tool Ma...
- Application Of Cutting Tools In The...
- Problems Of Tool
- Sustainable Development Of Green Cu...
- Melamine Tableware Is Harmful To Human
- Melamine Tableware You Can Radiate
- Melamine Tableware How To Identify ...
- 2017 CBME China Shanghai Expro
- How Are Ceramic Knives Made And The...
- KIND + JUGEND 2017 Cologne Trad Fair
- HK Baby Prduction Fair 2018